- Quantitative Study on the Refinement Behaviors of TiC Powders Produced by Mechanical Milling Under Different Impact Energy
-
Sung-Mo Hong, Eun-Kwang Park, Kyeong-Yeol Kim, Jin-Ju Park, Min-Ku Lee, Chang-Kyu Rhee, Jin-Kyu Lee, Young-Soon Kwon
-
J Korean Powder Metall Inst. 2012;19(1):32-39.
-
DOI: https://doi.org/10.4150/KPMI.2012.19.1.032
-
-
23
View
-
0
Download
-
5
Citations
-
 Abstract
 PDF
- This study investigated refinement behaviors of TiC powders produced under different impact energy conditions using a mechanical milling process. The initial coarse TiC powders with an average diameter of 9.3 µm were milled for 5, 20, 60 and 120 mins through the conventional low energy mechanical milling (LEMM, 22G) and specially designed high energy mechanical milling (HEMM, 65G). TiC powders with angular shape became spherical one and their sizes decreased as the milling time increased, irrespective of milling energy. Based upon the FE-SEM and BET results of milled powders, it was found initial coarse TiC powders readily became much finer near 100 nm within 60 min under HEMM, while their sizes were over 200 nm under LEMM, despite the long milling time of up to 120 min. Particularly, ultra-fine TiC powders with an average diameter of 77 nm were fabricated within 60 min in the presence of toluene under HEMM.
-
Citations
Citations to this article as recorded by  - Compaction and Sintering Characteristics of High Energy Ball Milled Mn-Zn Ferrite Powders
Hyunseung Lee, Hoseong Rhee, Sangsoo Lee, Si Young Chang
Korean Journal of Materials Research.2021; 31(12): 677. CrossRef - Fabrication of titanium carbide nano-powders by a very high speed planetary ball milling with a help of process control agents
Sung-Mo Hong, Jin-Ju Park, Eun-Kwang Park, Kyeong-Youl Kim, Jung-Gu Lee, Min-Ku Lee, Chang-Kyu Rhee, Jin Kyu Lee
Powder Technology.2015; 274: 393. CrossRef - Control of Y2O3 phase and its nanostructure formation through a very high energy mechanical milling
M.K. Lee, E.K. Park, J.J. Park, C.K. Rhee
Journal of Solid State Chemistry.2013; 201: 56. CrossRef - Fabrication of Fe coated Mg Based Desulfurization Powder by Mechanical Alloying Process
Joon-Woo Song, Otaduy Guillermo, Byong-Sun Chun, Soon-Jik Hong
Journal of Korean Powder Metallurgy Institute.2012; 19(3): 226. CrossRef - Synthesis and structural properties of Ni–20Cr–2Y2O3 nanocomposite alloy prepared by a very high energy mechanical milling
M.K. Lee, J.J. Park, C.K. Rhee
Materials Chemistry and Physics.2012; 137(1): 129. CrossRef
|
kpmi